PENGARUH VARIASI MEDIA QUENCHING TERHADAP KEKERASAN DAN STRUKTUR MIKRO Al-Si-Cu PADA BOGIE WHEEL
Penulis
MOCHAMAD TITO PRATAMA
Pembimbing : Nurfi Ahmadi, S.T.,M.Eng - Bahrul Jalaali, S.T.,M.Eng

ABSTRAK :
PENGARUH VARIASI MEDIA QUENCHING TERHADAP KEKERASAN DAN STRUKTUR MIKRO Al-Si-Cu PADA BOGIE WHEEL Ditulis oleh : MOCHAMAD TITO PRATAMA 16040009 Pembimbing 1 : Nurfi Ahmadi, S.T., M.Eng. Pembimbing 2 : Bahrul Jalaali, S.T., M.Eng. ABSTRAK Aluminium seri 3xx.x adalah aluminium kategori casting alloy (yaitu, paduan Al-Si-Cu) yang heat-treatable dan diaplikasikan dalam berbagai industri. Pada penelitian kali ini Al-Si-Cu dipilih untuk digunakan sebagai bahan pembuat bogie wheel tank amx-13. Untuk mendapatkan aluminium dengan karakter yang diinginkan harus melalui beberapa proses perlakuan salah satunya adalah heat treatment dan quenching. Penelitian ini bertujuan mengidentifikasi pengaruh variasi media quenching air, air garam dan oli SAE 40 terhadap kekerasan dan struktur mikro pada Al-Si-Cu yang dipanaskan selama 6 jam pada temperatur 540° C, lalu akan di-quenching dengan media pendingin masing-masing pada temperatur 65° C dengan waktu 10 menit. Hasil dari pengujian spesimen Al-Si-Cu menunjukkan bahwa tingkat kekerasan Al-Si-Cu pada proses quenching dengan lama pencelupan 10 menit menggunakan media (1) pendingin air adalah 75,484 BHN, (2) pendingin air garam adalah 74,748 BHN dan (3) pendingin oli Mesran SAE 40 adalah 74,285 BHN. Dengan demikian nilai rata-rata kekuatan tertinggi didapatkan dengan media quenching air sebesar 75,484 BHN. Kata kunci: quenching, media pendingin, Al-Si-Cu, bogie wheel, pengaruh variasi THE EFFECTS OF QUENCHING MEDIA VARIATIONS ON THE HARDNESS AND MICROSTRUCTURE OF Al-Si-Cu ON THE BOGIE WHEEL Written by: MOCHAMAD TITO PRATAMA 16040009 Supervisor 1 : Nurfi Ahmadi, S.T ., M.Eng. Supervisor 2 : Bahrul Jalaali, S.T ., M.Eng. ABSTRACT The 3xx.x series aluminum is a casting alloy aluminum category (i.e., Al-Si-Cu alloy) which is heat-treatable and has applications in a wide variety of industries. In this research, Al-Si-Cu was chosen to be used as a material for the amx-13 bogie wheel tank. To get aluminum with the desired character, it must go through several treatment processes, one of which is heat treatment and quenching. This research was aimed to investigate the effects of variations in water, salt water and SAE 40 oil quenching media on the hardness and microstructure of Al-Si-Cu heated for 6 hours at 540 ° C. They were quenched with cooling media each at a temperature of 65 ° C for 10 minutes. The results of testing the Al-Si-Cu speciment showed that the hardness level in the quenching process with immersion time of 10 minutes using (1) water cooling media was 75.484 BHN, (2) brine cooling media was 74.748 BHN and (3) Mesran SAE 40 oil cooling was 74.285 BHN. In conclusion, the highest average strength value was obtained with water quenching media of 75.484 BHN. Keywords: quenching, cooling media, Al-Si-Cu, bogie wheel, variation effect Approved by, Dewanti Ratna Pertiwi, S.Pd., M.Hum.


Tulisan Lengkap dapat Dibaca di Ruang Tesis/Disertasi
Penulis : MOCHAMAD TITO PRATAMA
NIM : 16040009
Foto :
File : [ Baca file skripsi ]
   

E-LibSTTA

Sistem Informasi Perpustakaan STTA Yogyakarta

© E-LibSTTA 2022